Nickel-based superalloys are the most widely used. The main reason is that, one is that more alloying elements can be dissolved in the nickel-based alloy, and it can maintain good structural stability; the other is that it can form a coherent and ordered A3B-type intermetallic compound γ[Ni3(Al, Ti)] As a strengthening phase, the alloy can be effectively strengthened and obtain higher high temperature strength than iron-based superalloys and cobalt-based superalloys; thirdly, nickel-based alloys containing chromium have better oxidation and resistance than iron-based superalloys.
Nickel-based alloys contain more than ten elements, of which Cr mainly plays an anti-oxidation and anti-corrosion role, and other elements mainly play a strengthening role. According to their strengthening action mode, they can be divided into: solid solution strengthening elements such as tungsten, molybdenum, cobalt, chromium and vanadium; precipitation strengthening elements such as aluminum, titanium, niobium and tantalum; grain boundary strengthening elements such as boron, zirconium, Magnesium and rare earth elements, etc.
Production Process
In terms of smelting: in order to obtain more pure molten steel, reduce gas content and harmful element content; at the same time, due to the presence of easily oxidizable elements such as Al and Ti in some alloys, it is difficult to control non-vacuum smelting; it is also to obtain better thermoplasticity , Nickel-based heat-resistant alloys are usually smelted in a vacuum induction furnace, and even produced by vacuum induction smelting plus vacuum consumable furnace or electroslag furnace remelting.
In terms of deformation: forging and rolling processes are used. For alloys with poor thermoplasticity, they are even rolled after extrusion and billeting or are directly extruded with mild steel (or stainless steel) sheathing. The purpose of deformation is to break the casting structure and optimize the microstructure.
Casting: usually use a vacuum induction furnace to smelt the master alloy to ensure the composition and control the gas and impurity content, and use the vacuum remelting-precision casting method to make parts.
Heat treatment: Wrought alloy and some cast alloys need to be heat treated, including solution treatment, intermediate treatment and aging treatment. Take Udmet 500 alloy as an example. Its heat treatment system is divided into four stages: solution treatment, 1175℃, 2 hours, Air cooling; intermediate treatment, 1080°C, 4 hours, air cooling; primary aging treatment, 843°C, 24 hours, air cooling; secondary aging treatment, 760°C, 16 hours, air cooling. In order to obtain the required organizational state and good overall performance.
About KMPASS
KMPASS is a trusted global chemical material supplier & manufacturer with over 12 years experience in providing super high-quality chemicals and Nanomaterials. The company export to many countries, such as USA, Canada, Europe, UAE, South Africa, Tanzania, Kenya,Egypt,Nigeria,Cameroon,Uganda,Turkey,Mexico,Azerbaijan,Belgium,Cyprus,Czech Republic,Brazil, Chile, Argentina, Dubai, Japan, Korea, Vietnam, Thailand, Malaysia, Indonesia, Australia,Germany, France, Italy, Portugal etc. As a leading nanotechnology development manufacturer, KMPASS dominates the market. Our professional work team provides perfect solutions to help improve the efficiency of various industries, create value, and easily cope with various challenges. If you are looking for Inconel718 powder, please send an email to: sales2@nanotrun.com